Deskripsyon pwodwi
Mgo c brik se te fè soti nan mayezi fusion, mayezi-wo pite ak grafit, epi yo fòme pa bòdi presyon ki wo ak tretman tanperati ki ba. Diferan klas brik mgo c ka chwazi selon kondisyon fusion diferan, lavi sèvis nan chalè ak klas asye fusion.
Avantaj nan CH refractories:
CH refractories pral bay konsepsyon gratis nan pawa mgo c brik pou louch ou a, (EAF) elektrik arc founo refractory pawa ak refractory gwo founo dife, selon kondisyon travay founo ou ak egzijans chalè, rafine tan pou garanti lavi sèvis.
mgo c brik ki fabrike pa CH Refractories gen anpil pwopriyete ekselan mekanik tankou fòs segondè, segondè severite ak dite segondè. Nan anviwònman piman bouk tankou tanperati ki wo ak presyon ki wo, brik mayezyòm-kabòn ka kenbe entegrite ak fòs nan estrikti a ak efektivman reziste presyon ekstèn ak enpak.
Aplikasyon mgo c brik:
se mgo c brik lajman ki itilize nan asye, elektwoliz aliminyòm, pétrochimique ak lòt endistri yo, paske yo gen ekselan tanperati ki wo, rezistans korozyon, rezistans mete, segondè fòs ak karakteristik konduktiviti elektrik.
Endèks fizik ak chimik
|
Mak |
MT-12A |
MT-12B |
MT-12C |
MT-14A |
MT-14B |
MT-14C |
|
MgO/% Pi gran pase oswa egal a |
78 |
76 |
74 |
76 |
74 |
72 |
|
C/% Pi gran pase oswa egal a |
12 |
12 |
12 |
14 |
14 |
14 |
|
Porosite aparan/% mwens pase oswa egal a |
4 |
5 |
6 |
4 |
5 |
6 |
|
Dansite esansyèl g/cm3 Pi gran pase oswa egal a |
2.98 |
2.96 |
2.98 |
2.98 |
2.96 |
2.95 |
|
Fòs kraze/Mpa Pi gran pase oswa egal a |
40 |
40 |
40 |
40 |
40 |
35 |
|
Modil cho nan rupture (1450 degre) / Mpa |
8 |
7 |
6 |
12 |
10 |
8 |
Pakè:
Endèks fizik ak chimik
|
Mak |
MT-12A |
MT-12B |
MT-12C |
MT-14A |
MT-14B |
MT-14C |
|
MgO/% Pi gran pase oswa egal a |
78 |
76 |
74 |
76 |
74 |
72 |
|
C/% Pi gran pase oswa egal a |
12 |
12 |
12 |
14 |
14 |
14 |
|
Porosite aparan/% mwens pase oswa egal a |
4 |
5 |
6 |
4 |
5 |
6 |
|
Dansite esansyèl g/cm3 Pi gran pase oswa egal a |
2.98 |
2.96 |
2.98 |
2.98 |
2.96 |
2.95 |
|
Fòs kraze/Mpa Pi gran pase oswa egal a |
40 |
40 |
40 |
40 |
40 |
35 |
|
Modil cho nan rupture (1450 degre) / Mpa |
8 |
7 |
6 |
12 |
10 |
8 |